Adsyl 7622 XCP
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adsyl |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6RRXzi_Adsyl7622XCP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adsyl 7622 XCP is an advanced polyolefin, specially designed for use as a sealing or metallized layer in co-extruded film applications. This grade features a very low seal initiation temperature and good optics. It does not contain slip or anti-block additives. For regulatory information please refer to Adsyl 7622 XCP Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.5 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3/25 | ||
| MD : 50 µm, cast film | 280 | MPa | ISO 527-3/25 |
| TD : 50 µm, cast film | 280 | MPa | ISO 527-3/25 |
| Tensile Stress | ISO 527-3/500 | ||
| MD : yield, 50 µm, cast film | 14.0 | MPa | ISO 527-3/500 |
| TD : yield, 50 µm, cast film | 14.0 | MPa | ISO 527-3/500 |
| MD : fracture, 50 µm, casting film | 45.0 | MPa | ISO 527-3/500 |
| TD : fracture, 50 µm, casting film | 35.0 | MPa | ISO 527-3/500 |
| Tensile Elongation | ISO 527-3/500 | ||
| MD : yield, 50 µm, cast film | 17 | % | ISO 527-3/500 |
| TD : yield, 50 µm, cast film | 15 | % | ISO 527-3/500 |
| MD : fracture, 50 µm, casting film | 900 | % | ISO 527-3/500 |
| TD : fracture, 50 µm, casting film | 800 | % | ISO 527-3/500 |
| Seal Initiation Temperature | 105 | °C |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 62.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 107 | °C | ISO 306/A50 |
| Melting Temperature | 132 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm) | 88 | ASTM D2457 | |
| Haze (50.0 µm) | 0.60 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP M1316 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Sylvin 6169-89 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Jiangsu Sinarise ZM928 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| Kaneka MUH M3100 | Kaneka Corporation | ABS | Kaneka MUH |
| Thermec S™ 6250R60 | Technical Polymers, LLC | PPS | Thermec S™ |