SEPAZ™ 100L
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | SEPAZ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6QGhDg_SEPAZ-100L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SEPAZ™ 100L is a Polyphthalamide (PPA) product. It is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow | 0.50 | % | |
| Across Flow | 0.70 | % | |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 86.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 3740 | MPa | ASTM D790 |
| Flexural Strength | 157 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 15 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 138 | °C | ASTM D648 |
| Peak Melting Temperature | 313 | °C | ASTM D2133 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 300 to 330 | °C | |
| Mold Temperature | 130 to 160 | °C |
| Note Message | |
|---|---|
| 1 . | 60°C Mold Temperature |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecnoflon® N 535 | Solvay Specialty Polymers | Fluorelastomer | Tecnoflon® |
| SUMILITE® PL-1621 (Machining) | Sumitomo Bakelite Co., Ltd. | Phenolic | SUMILITE® |
| Viton® B-600 | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| TOTAL Polypropylene PPC 12712 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Plaslube® J-1/30/TF/22 NAT | Techmer Engineered Solutions | Nylon 66 | Plaslube® |