Makrolon® AX2677
| Category: | PC , Polycarbonate |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makrolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6PiCmN_MakrolonAX2677.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MVR (300 °C/1.2 kg) 12 cm³/10 min; medium viscosity; easy release; UV stabilized; injection molding - melt temperature 280 - 320 °C; available in black colors only; automotive exterior roof trim + pillar appliques; optimized and especially suitable for high-gloss surfaces with highest requirements "Piano-black"; tailored for the use in combination with Polysiloxan coatings |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.20 | g/cm³ | ISO 1183 |
| Apparent Density 1 | 0.66 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 13 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Transverse flow | 0.60 - 0.80 | % | ISO 2577 |
| Flow | 0.60 - 0.80 | % | ISO 2577 |
| Transverse flow : 2.00mm 2 | 0.75 | % | ISO 294-4 |
| Flow : 2.00mm 3 | 0.70 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.12 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 115 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 65.0 | MPa | ISO 527-2/50 |
| Fracture, 23°C | 69.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 6.0 | % | ISO 527-2/50 |
| Fracture, 23°C | 120 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 4(23°C) | 2400 | MPa | ISO 178 |
| Flexural Stress 5 | ISO 178 | ||
| 23°C | 98.0 | MPa | ISO 178 |
| 3.5% strain, 23°C | 74.0 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 6(23°C) | 7.1 | % | ISO 178 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Application of Flame from Small Burner - Method K and F (2.00 mm) | K1, F1 | DIN 53438-1, -3 | |
| Flash Ignition Temperature | 480 | °C | ASTM D1929 |
| Self Ignition Temperature | 550 | °C | ASTM D1929 |
| Combustion rate- US-FMVSS (> 1.00 mm) | passed | ISO 3795 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Electrolytical Corrosion (23°C) | A1 | IEC 60426 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Vapor Transmission Rate (23°C, 85% RH, 100 µm) | 15 | g/m²/24 hr | ISO 15106-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7 | ISO 7391 | ||
| -30°C, complete fracture | 16 | kJ/m² | ISO 7391 |
| 23°C, local fracture | 70 | kJ/m² | ISO 7391 |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -60°C | No Break | ISO 179/1eU | |
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact 8 | ISO 7391 | ||
| -30°C, complete fracture | 15 | kJ/m² | ISO 7391 |
| 23°C, local fracture | 70 | kJ/m² | ISO 7391 |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30°C | 60.0 | J | ISO 6603-2 |
| 23°C | 55.0 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | ||
| -30°C | 6100 | N | ISO 6603-2 |
| 23°C | 5200 | N | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 123 | °C | ISO 75-2/A |
| Glass Transition Temperature 9 | 142 | °C | ISO 11357-2 |
| Vicat Softening Temperature | |||
| -- | 142 | °C | ISO 306/B50 |
| -- | 143 | °C | ISO 306/B120 |
| Ball Pressure Test (135°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity 10(23°C) | 0.20 | W/m/K | ISO 8302 |
| RTI Elec (1.5 mm) | 125 | °C | UL 746 |
| RTI Imp (1.5 mm) | 115 | °C | UL 746 |
| RTI (1.5 mm) | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | 34 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.10 | IEC 60250 | |
| 23°C, 1 MHz | 3.00 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 5.0E-4 | IEC 60250 | |
| 23°C, 1 MHz | 9.0E-3 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | ||
| Solution a | 250 | V | IEC 60112 |
| Solution B | 125 | V | IEC 60112 |
| Note Message | |
|---|---|
| 1 . | Pellets |
| 2 . | 60x60x2 mm, 500 bar |
| 3 . | 60x60x2 mm, 500 bar |
| 4 . | 2.0 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 2 mm/min |
| 7 . | Based on ISO 179-1eA, 3 mm |
| 8 . | Based on ISO 180-A, 3 mm |
| 9 . | 10°C/min |
| 10 . | Cross-flow |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adflex X 500 F | LyondellBasell Industries | Polyolefin, Unspecified | Adflex |
| ALTECH® PP-B A 3030/500 GB30 | ALBIS PLASTIC GmbH | PP Copolymer | ALTECH® PP-B |
| Geon™ Fiberloc™ 80510 | PolyOne Corporation | PVC, Rigid | Geon™ Fiberloc™ |
| Kepital® TE-23(FU2015) | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| Lupoy® NF1009F 15 | LG Chem Ltd. | PC | Lupoy® |