Sasol Polymers PP HSV103

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	Sasol Polymers
Trademark:	Sasol Polymers PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	6PBloW_Sasol-Polymers-PP-HSV103.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Features

High flow

Narrow molecular weight distribution

Offers easy extrusion processability when used for producing:

Spunbonded non-woven materials

BCF carpet yarn on in-line or two stage spin / draw / wind or short spin / warp draw / wind processes

Continuous filament (CF) on multi position spin / draw / wind processes

Applications
Extrusion

Spunbond fabric for industrial applications (roofing membranes, geotextiles)

Spunbond fabrics for hygiene applications (nappy liners, medical gowns and masks)

Carpet yarns

Extrusion coating of woven PP cloth

Hair braids

General Information
Additive	Anti-gas fading Processing Stabilizer
Features	Food Contact Acceptable Gas-fading Resistant Good Processability Good Processing Stability High Flow Homopolymer Narrow Molecular Weight Distribution
Uses	BCF Yarn Fabrics Filaments Industrial Applications Spunbond Nonwovens Wovens Coatings
Agency Ratings	EC 1935/2004 FDA 21 CFR 177.1520(a)(3)(i)(c)(1) FDA 21 CFR 177.1520(c) 3.1a
Forms	Pellets
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.905	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	30	g/10 min	ISO 1133

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	68.0	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1400	MPa	ISO 527-2/1A/1
Tensile Stress (Yield)	32.0	MPa	ISO 527-2/1A/50
Tensile Strain			ISO 527-2/1A/50
Yield	8.5	%
Break	> 50	%
Flexural Modulus	1350	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	2.5	kJ/m²	ISO 179/1eA

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	83.0	°C	ISO 75-2/B
1.8 MPa, Unannealed	52.0	°C	ISO 75-2/A
Vicat Softening Temperature
--	152	°C	ISO 306/A120
--	88.0	°C	ISO 306/B120
Melting Temperature	163	°C	ISO 11357-3

Extrusion	Nominal Value	Unit
Hopper Temperature	40.0 to 60.0	°C
Cylinder Zone 1 Temp.	200 to 280	°C
Cylinder Zone 2 Temp.	240 to 280	°C
Cylinder Zone 3 Temp.	240 to 280	°C
Cylinder Zone 4 Temp.	240 to 280	°C
Cylinder Zone 5 Temp.	220 to 280	°C
Melt Temperature	220 to 280	°C
Die Temperature	220 to 240	°C

Resin Grade	Manufacturer	Category	Trademark
Texalan® 3 Series 382A	Austin Novel Materials Co. Ltd.	TPU-Polyester	Texalan® 3 Series
Alathon® M6080WC	LyondellBasell Industries	HDPE	Alathon®
HIVAL® 5303	Nexeo Solutions, LLC.	PS (HIPS)	HIVAL®
LEXAN™ HPX8R resin	SABIC Innovative Plastics	PC	LEXAN™
Lionpol HF-209582	Lion Polymers Incorporated	TPE	Lionpol