Braskem PP H362-09RS
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Braskem Europe GmbH |
| Trademark: | Braskem PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6Mr9nD_Braskem-PP-H362-09RS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Braskem H362-09RS Polypropylene Resin is a homopolymer suited for high output, fast running cast film lines. It is mostly used in the production of transparent films with a thickness range of 15-150µm and contains oleamide as slip additive. Braskem H362-09RS Polypropylene Resin has an optimized rheology for fast extrusion capability and allows for easy film winding, as well as good printability after corona treatment. Films based on Braskem H362-09RS Polypropylene Resin exhibit excellent optical properties, notably transparency and gloss. Applications for Braskem H362-09RS Polypropylene Resin:
Regulatory Information Braskem H362-09RS Polypropylene should comply with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, Injection Molded) | 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, Injection Molded) | 12 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 1200 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 50 µm, Cast Film | 632 | MPa | |
| 1% Secant, TD : 50 µm, Cast Film | 703 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 50 µm, Cast Film | 39.0 | MPa | |
| TD : Break, 50 µm, Cast Film | 28.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm, Cast Film | 530 | % | |
| TD : Break, 50 µm, Cast Film | 520 | % | |
| Dart Drop Impact (50 µm, Cast Film) | 190 | g | ISO 7765-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 5.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 151 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Cast Film) | 75 | ASTM D2457 | |
| Haze (50.0 µm, Cast Film) | 5.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Measured on cast film with a thickness of 50 micron |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PP5120R B2 | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| NEFTEKHIM PP 1548R | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| LEXAN™ EXL9330 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Karina IVORY PVC COMPOUND 105905-35/ 1-BY-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polifil® PP RMT-30 | The Plastics Group | PP Impact Copolymer | Polifil® PP |