Generic PP Impact Copolymer
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6IaAuG_Generic-PP-Impact-Copolymer.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP Impact Copolymer This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.892 - 0.902 | g/cm³ | ASTM D792 |
| 23°C | 0.898 - 0.907 | g/cm³ | ISO 1183 |
| -- | 0.900 - 0.906 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 0.30 - 37 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 0.20 - 25 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 1.80 - 135 | cm³/10min | ISO 1133 |
| Spiral Flow | 79.1 - 80.0 | cm | |
| Molding Shrinkage | |||
| Flow : 23°C | 1.2 - 1.7 | % | ASTM D955 |
| Transverse flow : 23°C | 1.4 - 1.7 | % | ASTM D955 |
| 23°C | 1.2 - 1.9 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 75 - 106 | ASTM D785 | |
| 23°C | 70 - 105 | ISO 2039-2 | |
| Durometer Hardness | |||
| 23°C | 21 - 71 | ASTM D2240 | |
| 23°C | 59 - 66 | ISO 868 | |
| Ball Indentation Hardness | 42.0 - 69.7 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1000 - 1510 | MPa | ASTM D638 |
| 23°C | 975 - 1620 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 19.3 - 30.7 | MPa | ASTM D638 |
| Yield, 23°C | 19.5 - 29.3 | MPa | ISO 527-2 |
| Fracture, 23°C | 17.3 - 19.8 | MPa | ASTM D638 |
| Fracture, 23°C | 12.5 - 18.1 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 3.0 - 13 | % | ASTM D638 |
| Yield, 23°C | 3.4 - 12 | % | ISO 527-2 |
| Fracture, 23°C | 2.0 - 520 | % | ASTM D638 |
| Fracture, 23°C | 45 - 510 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 844 - 1560 | MPa | ASTM D790 |
| 23°C | 898 - 1570 | MPa | ISO 178 |
| Flexural Strength (23°C) | 24.5 - 43.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.6 - 52 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 4.4 - 180 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 39 - 160 | J/m | ASTM D256 |
| 23°C | 3.5 - 53 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 59 - 140 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 12.7 - 24.8 | J | ASTM D3029 |
| Dart Drop Impact (23°C) | 27.7 - 36.2 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 78.4 - 127 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 68.9 - 107 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 104 - 124 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 48.2 - 60.3 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 46.9 - 56.4 | °C | ISO 75-2/A |
| Ductile / Brittle Transition Temperature | -60.0 - -45.0 | °C | ISO 6603-2 |
| Vicat Softening Temperature | |||
| -- | 145 - 153 | °C | ASTM D1525 |
| -- | 64.5 - 155 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 140 - 166 | °C | |
| -- | 163 | °C | ISO 11357-3 |
| -- | 165 | °C | ISO 3146 |
| RTI Elec | 65.0 - 116 | °C | UL 746 |
| RTI Imp | 65.0 - 116 | °C | UL 746 |
| RTI | 65.0 - 116 | °C | UL 746 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 28 - 77 | ASTM D2457 | |
| Haze | 80 - 82 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 185 - 223 | °C | |
| Middle Temperature | 194 - 250 | °C | |
| Front Temperature | 203 - 260 | °C | |
| Nozzle Temperature | 239 - 251 | °C | |
| Processing (Melt) Temp | 209 - 250 | °C | |
| Mold Temperature | 34.9 - 49.8 | °C | |
| Injection Pressure | 4.41 - 172 | MPa | |
| Holding Pressure | 33.4 - 152 | MPa | |
| Screw Speed | 55 - 56 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP Impact CopolymerThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 214 - 231 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP Impact CopolymerThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TITANPRO® L-670M | Lotte Chemical Titan (M) Sdn. Bhd. | PP Random Copolymer | TITANPRO® |
| ADEKA F7-67 | Adeka Corporation | PUR-Ester | ADEKA |
| Gallonprene® GP420-6501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Sylvin 9067-65 Orange 593 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ 144R resin | SABIC Innovative Plastics | PC | LEXAN™ |