ALCUDIA® LDPE TR-135
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6HihlH_ALCUDIA-LDPE-TR-135.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCUDIA® TR-135 natural compound is an hexene copolymer of high molecular weight especially apt for the extrusion of pipe. Because other good mechanical properties and their characteristics, the polyethylene natural compound ALCUDIA® TR-135, is designed to produce pipe. It has the antioxidant package enough for the extrusion process. This product is supplied in natural colour but they can be easily coloured with pigments steady at processing temperature, using dry-colouring or masterbatch techniques. ALCUDIA® TR-135 is a medium density polyethylene grade, high molecular weight hexene copolymer, especially intended for film extrusion. This material offers easy processability into films with excellent mechanical properties, good sealing characteristics and high stress crack resistance. It contains antioxidant additives. TYPICAL APPLICATIONS
Recommended melt temperature range from 190 to 220°C. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.938 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.12 | g/10 min | ISO 1133 |
| 190°C/21.6 kg | 12 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.60 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (10% Antarox CO-630, F50) | > 4000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 20.0 | MPa | ASTM D638 |
| Fracture | 30.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 13 | % | ASTM D638 |
| Fracture | 800 | % | ASTM D638 |
| Flexural Modulus | 700 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 1500 µm, cast film | 18.0 | MPa | ISO 527-3 |
| TD : Yield, 1500 µm, cast film | 20.0 | MPa | ISO 527-3 |
| MD : 1500 µm, cast film | 33.0 | MPa | ISO 527-3 |
| TD : 1500 µm, cast film | 35.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture, 1500 µm, cast film | 750 | % | ISO 527-3 |
| TD : Fracture, 1500 µm, cast film | 900 | % | ISO 527-3 |
| Dart Drop Impact (20 µm, Blown Film) | 120 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 20 µm, blown film | 0.20 | N | ISO 6383-2 |
| TD : 20 µm, blown film | 5.8 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -118 | °C | ASTM D746 |
| Vicat Softening Temperature | |||
| -- | 126 | °C | ASTM D1525 1 |
| -- | 115 | °C | ISO 306/A |
| Melting Temperature | 133 | °C | ISO 11357-3 |
| Additional Information |
|---|
| Blown film data taken from 20µm film with a blow up ratio of 3:1 and a frost line height of 70 cm. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 175 - 195 | °C | |
| Cylinder Zone 2 Temp. | 180 - 200 | °C | |
| Cylinder Zone 3 Temp. | 185 - 205 | °C | |
| Cylinder Zone 4 Temp. | 190 - 210 | °C | |
| Cylinder Zone 5 Temp. | 190 - 210 | °C | |
| Melt Temperature | 195 - 215 | °C |
| Note Message | |
|---|---|
| 1 . | 速率 A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NaturePlast PLI 003 | NaturePlast | PLA | NaturePlast |
| NYLOY® MC-0030N | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |
| Colorite 88 Series 7088 | Colorite Polymers | PVC, Unspecified | Colorite 88 Series |
| G-Lex F55HM0003 | Gas Authority of India Limited | HDPE, HMW | G-Lex |
| HiFill FR® ABS FR AS | Techmer Engineered Solutions | ABS | HiFill FR® |