KOPELEN JH-370A
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | KOPELEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6HMi3G_KOPELEN-JH-370A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
JH-370A is high impact block copolymer with high ethylene content as co-monomer. This grade is designed to be processed in conventional Injection molding equipment and base resin for compounding. JH-370A shows extremely high impact resistance at low temperature and has also high strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 27 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 22.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 100 | % | ASTM D638 |
| Flexural Modulus | 1230 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -10°C | 49 | J/m | |
| 23°C | 98 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 105 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AIE PP 80T10 | Asia International Enterprise (Hong Kong) Limited | PP, Unspecified | AIE PP |
| Axiall PVC 12720 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Axiall PVC 7181 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| LONGLITE® PBT 6030-104X | CCP Group | PC+PBT | LONGLITE® PBT |
| MAJORIS EX870 | AD majoris | PP, Unspecified | MAJORIS |