Plaslube® PEI CF30 TL15
| Category: | PEI , Polyether Imide |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6FnHKI_Plaslube-PEI-CF30-TL15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plaslube® PEI CF30 TL15 is a Polyether Imide (PEI) product filled with 30% carbon fiber. It can be processed by injection molding and is available in North America. Primary characteristic: lubricated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 203 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 17200 | MPa | ASTM D790 |
| Flexural Strength | 269 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.19 | ||
| vs. Steel - Static | 0.20 | ||
| Wear Factor | 71 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 96 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 213 | °C | |
| 1.8 MPa, Unannealed | 210 | °C | |
| CLTE - Flow | 1.6E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+7 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 141 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 357 to 391 | °C | |
| Middle Temperature | 357 to 391 | °C | |
| Front Temperature | 357 to 391 | °C | |
| Processing (Melt) Temp | 354 to 388 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRISTAR® PC-10R-(6) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| Xuchuan XCS-2150EN | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| UNITIKA Nylon 66 A125 | UNITIKA Plastics Division | Nylon 66 | UNITIKA Nylon 66 |
| Kumho ABS HU650ZW | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |
| KRATON® D1164 P | Kraton Polymers LLC | SIS | KRATON® |