SILVER® PE 1011.LDH
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Guangdong Silver Age Sci & Tech. Co., Ltd |
| Trademark: | SILVER® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6F0iin_SILVER-PE-1011-LDH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SlLVER® Modified Polyolefin includes modified polyethylene and modified polypropylene. Modified polyethylene is mainly applied to cable jacket. Black polyethylene compound is composed of polyethylene resin,carbon black, antioxidantand so on. Black polyehylene compound is applied to communication cable,contoll cable,signal cable,power cable,opticalcable and submarine cable. It conforms to GB15065-94 Standard. Modified PP including flame resistant, glass fiber andmineral reinforced and weather—resistant, is widely applied in electronic & electrical appliances, household appliances, autoaccessories, lightings, mechanical components and sockets, and so on. In addition, we develop new products according to customer's specific requirements. Characteristics:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 0.918 to 0.943 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | < 2.0 | g/10 min | |
| Environmental Stress-Cracking Resistance (F0) | > 500 | hr | |
| Carbon Black Content | 2.4 to 2.9 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Oxidation Induction Time (200°C) | > 30 | min |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Extruder Screw L/D Ratio | 22.0:1.0 to 26.0:1.0 |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength | > 14.0 | MPa | |
| Tensile Elongation 1(Break) | > 600 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C |
| Electrical | Nominal Value | Unit | |
|---|---|---|---|
| Volume Resistivity | > 1.0E+6 | ohms·cm | |
| Dielectric Strength | > 25 | kV/mm | |
| Dielectric Constant (1 MHz) | < 2.80 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 170 to 175 | °C | |
| Cylinder Zone 3 Temp. | 175 to 180 | °C | |
| Cylinder Zone 5 Temp. | 180 to 185 | °C | |
| Die Temperature | 185 to 190 | °C |
| Note Message | |
|---|---|
| 1 . | 100 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 TFE 5 | RTP Company | PC | RTP |
| YUNGSOX® PP 3080 | Formosa Polypropylene | PP Impact Copolymer | YUNGSOX® PP |
| Excelprene® GFE-1810 | S&E Specialty Polymers, LLC | PVC+NBR | Excelprene® |
| Hyundai EP Adhesives LE851P/1002 | HYUNDAI EP Co., Ltd. | PE, Unspecified | Hyundai EP Adhesives |
| K-Bin Rigid PVC KBD-5008N | K-Bin, Inc. | PVC, Unspecified | K-Bin Rigid PVC |