Cabofor® 28 GF/30 NATURALE
| Category: | PC , Polycarbonate |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Cabofor® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6ErsnG_Cabofor-28-GF-30-NATURALE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fiber reinforced polycarbonate grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.30 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 130 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 8000 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 80 | J/m | |
| 0°C | 100 | J/m | |
| 23°C | 110 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 139 | °C | ASTM D648 |
| Vicat Softening Temperature | 147 | °C | ASTM D1525 1 |
| Ball Pressure Test (125°C) | Pass | IEC 335 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | V-1 | ||
| 3.20 mm | V-1 | ||
| Glow Wire Ignition Temperature | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 32 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 280 | °C | |
| Front Temperature | 300 | °C | |
| Mold Temperature | 100 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermoset Plastics 286 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| Karina BLACK PVC COMPOUND 809D48/1-C-AC-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lucent PP CPP-320 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |
| HiFill® HiFill® 1-10815 | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Elastocon® STK50B | Elastocon TPE Technologies | TPE | Elastocon® |