Nypol® PA A3 G15 P7 M1 S1 NTLA014 NR335
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6EU9S5_Nypol-PA-A3-G15-P7-M1-S1-NTLA014-NR335.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 natural reinforced with 15% of fiberglass, 7% PTFE, lubricated with molybdenum disulfide and silicon, good set of thermal and mechanical properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.35 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 to 0.90 | -- | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.3 | -- | % | ASTM D570 |
| Ash Content | 13 to 17 | -- | % | ASTM D2584 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 120 | 90.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | 8.0 | % | ASTM D638 |
| Flexural Modulus | 4900 | 2700 | MPa | ASTM D790 |
| Flexural Strength | 165 | 115 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 42 | 50 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 238 | -- | °C | ASTM D648 |
| Melting Temperature | 250 to 265 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 | 1.0E+13 | ohms·cm | ASTM D257 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | V-0 | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CALP HG2310A | Lion Idemitsu Composites Co., Ltd. | Nylon, Unspecified | CALP |
| Hanwha Total PP B230D | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, HMS | Hanwha Total PP |
| King Pearl® F Series | Loyal Chemical | PS (EPS) | King Pearl® |
| Sylvin 8200-88 White 1523 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ STAT-KON™ DEL22P compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |