Wellamid® GFT15N050-WBK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Wellman Engineering Resins |
| Trademark: | Wellamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6DhTRz_Wellamid-GFT15N050-WBK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Wellamid® GFT15N050-WBK is a Polyamide 66 (Nylon 66) material filled with 15% glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America. Important attributes of Wellamid® GFT15N050-WBK are:
Typical application of Wellamid® GFT15N050-WBK: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 0.90 to 1.3 | % | |
| Flow : 23°C | 1.0 to 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 3.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 115 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 11 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 215 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACRYLITE® LED 8N LD96 | Evonik Cyro LLC | Acrylic (PMMA) | ACRYLITE® |
| CABELEC® CA4743 | Cabot Corporation | HDPE | CABELEC® |
| KEBATER® PBT A0130 | BARLOG plastics GmbH | ABS+PBT | KEBATER® |
| SABIC® HDPE CC2056 | Saudi Basic Industries Corporation (SABIC) | HDPE Copolymer | SABIC® HDPE |
| LGG 1046 | LG Polymers India Pvt. Ltd. | PS (GPPS) | LGG |