RheTech Thermoplastic Polyolefin FT7030-01UVEG
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | RheTech, Inc. |
| Trademark: | RheTech Thermoplastic Polyolefin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6BKr29_RheTech-Thermoplastic-Polyolefin-FT7030-01UVEG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoplastic Polyolefin, 275K Flexural Modulus, UV Stabilized, Black, Extrusion Grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.3 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 67 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 24.1 | MPa | ASTM D638 |
| Flexural Modulus | 1900 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 130 | J/m | ASTM D256 |
| Dart Drop Impact | 15.8 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 111 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 56.7 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 - 82.2 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 193 - 221 | °C | |
| Middle Temperature | 199 - 227 | °C | |
| Front Temperature | 204 - 232 | °C | |
| Nozzle Temperature | 199 - 227 | °C | |
| Mold Temperature | 21.1 - 65.6 | °C | |
| Injection Pressure | 2.76 - 10.3 | MPa | |
| Holding Pressure | 2.07 - 8.27 | MPa | |
| Back Pressure | 0.345 - 1.03 | MPa |
| Injection instructions |
|---|
| Injection Speed: Variable - application dependentScrew RPM: Recovery 3 seconds before mold opensCycle Time: Wall thickness dependent |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Talcoprene® 520TL LE NERO | SO.F.TER. SPA | PP Homopolymer | Talcoprene® |
| Galloo GP-PP-1065 | Galloo Plastics | PP, Unspecified | Galloo |
| ELASTOSIL® LR 3094/60 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Epolene® C-23 | Westlake Chemical Corporation | LDPE | Epolene® |
| KOPA® KN133HI | Kolon Plastics, Inc. | Nylon 6 | KOPA® |