VENELENE® 11PG4
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Poliolefinas Internacionales, C.A. (Polinter) |
| Trademark: | VENELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6AlxZO_VENELENE-11PG4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Features:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.1 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 35 | µm | |
| Film Puncture Force (35 µm) | 4.31 | N | ASTM D3420 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 35 µm | 35.0 | MPa | ASTM D882 |
| TD : Fracture, 35 µm | 30.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 35 µm | 700 | % | ASTM D882 |
| TD : Fracture, 35 µm | 800 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 35 µm | 300 | g | ASTM D1922 |
| TD : 35 µm | 450 | g | ASTM D1922 |
| Impact Resistance, Film | 230 | J/cm | ASTM D1709 |
| Toughness, Film | ASTM D882 | ||
| MD | 120 | MPa | ASTM D882 |
| TD | 135 | MPa | ASTM D882 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 80.0 | % | ASTM D1003 |
| Haze | 15 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 210 | °C |
| Extrusion instructions |
|---|
| Inverted Extrusion profile (descendent). Blow up ratio (BUR):2 - 3. Die gap: 0.9 - 1.5 mm. Frost line Height: 4 to 5 times Die diameter. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 1088B | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| Mowiol® 28-99 LA | Kuraray Co., Ltd. | PVOH | Mowiol® |
| TRISTAR® PC-10R-(18) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| ALTECH® PA6 A 2015/220 GF15 UV | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| OXNILON 66 36MIN-5IMP-BK | Oxford Polymers | Nylon 66 | OXNILON 66 |