TORZEN® G3500HR BK34
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | INVISTA Engineering Polymers |
| Trademark: | TORZEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6Ak8Bf_TORZENG3500HRBK34.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TORZEN® G3500HR BK34 is a 35% glass reinforced, heat stabilized, black, PA66 resin suitable for hydrolysis resistant applications as well as many injection molding applications where high tensile strength and dimensional stability are needed. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow : 2.00mm | 0.90 - 1.1 | % | ISO 294-4 |
| Flow : 2.00mm | 0.25 - 0.35 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.1 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.7 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 210 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 10500 | MPa | ISO 178 |
| Flexural Stress | 300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 10 | kJ/m² | ISO 179 |
| 23°C | 12 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 12 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 260 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 250 | °C | ISO 75-2/A |
| Melting Temperature | 262 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.080 - 0.18 | % | |
| Rear Temperature | 250 - 270 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 270 - 290 | °C | |
| Nozzle Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 50 - 90 | °C | |
| Back Pressure | 0.200 - 1.00 | MPa | |
| Cushion | 4.00 - 6.00 | mm | |
| Vent Depth | 7.0E-3 - 0.040 | mm | |
| Screw Speed | Low rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polystyrene Impact 3630 | TOTAL Refining & Chemicals | PS (MIPS) | TOTAL Polystyrene |
| YUZEX® 2500A | SK Global Chemical | HDPE | YUZEX® |
| AKROMID® B3 GF 15 9 RM-M black (3512) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| HiFill® HDPE TM20 | Techmer Engineered Solutions | HDPE | HiFill® |
| Lanufene HBD-5224 | Ras Lanuf Oil & Gas Processing Company (RASCO) | HDPE | Lanufene |