Hysol® 9432NA
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Loctite® |
| Trademark: | Hysol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6ATn5I_Hysol-9432NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Loctite® Hysol® 9432NA is an aluminum filled, thixotropic, one component epoxy adhesive. Hysol 9432NA is formulated to provide excellent tensile shear strength over a wide range of temperatures and a high degree of impact resistance. This adhesive can bond oily and other poorly prepared surfaces and can be used to bond a wide variety of substrates. Hysol 9432NA is designed to cure at moderate temperatures but has a long shelf life at room temperature. This adhesive can be easily pumped and dispensed onto parts without sagging due to its high thixotrophy. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.38 | g/cm³ | |
| Density | 1.378 | g/cm³ | |
| Viscosity | 150 to 300 | Pa·s |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shear Strength 2 | ASTM D1002 | ||
| Budd Company Fiberglass SMC : 25°C | 2.62 | MPa | |
| CR Steel Abraded : 25°C | 20.7 | MPa | |
| CR Steel Degreased : 25°C | 19.7 | MPa | |
| CR Steel Oily : 25°C | 17.9 | MPa | |
| Degreased Aluminum : 25°C | 24.1 | MPa | |
| Etched Aluminum : -55°C | 24.1 | MPa | |
| Etched Aluminum : 25°C | 26.2 | MPa | |
| Etched Aluminum : 121°C | 20.7 | MPa | |
| Etched Aluminum : 149°C | 16.5 | MPa | |
| Etched Aluminum : 177°C | 2.76 | MPa | |
| Etched Aluminum : 204°C | 2.76 | MPa | |
| Fiberglass Vinyl Ester Laminate : 25°C | 6.89 | MPa | |
| Owens Corning Fiberglass SMC : 25°C | 2.76 | MPa | |
| Slump (149°C) | < 7.62 | mm |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4690 | MPa | ASTM D638 |
| Tensile Strength | 50.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.2 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | 77°F |
| 2 . | Cured 30 minutes at 300°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP GP3203 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| AMTOPP WA30 | Inteplast Group | PP, Unspecified | AMTOPP |
| Kumho SBR 1502 | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |
| MAJORIS FG308X - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| Sylvin 9067F3 Red 6270 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |