Plexiglas® Diffuse™ DR®-66151
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Altuglas International of Arkema Inc. |
| Trademark: | Plexiglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 697dsQ_PlexiglasDiffuseDR66151.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plexiglas® Diffuse™ DR®-66151 is a thermoplastic acrylic resin sufficiently concentrated to be used in blend formulations via extrusion to tailor lens properties in the LED lighting market. It is characterized by its outstanding hiding performance and high impact resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 - 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 1.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 - 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 38 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ASTM D638 |
| Tensile Strength (Break) | 39.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 45 | % | ASTM D638 |
| Flexural Modulus | 1600 | MPa | ASTM D790 |
| Flexural Strength (Break) | 59.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1 | ASTM D648 | ||
| 0.45 MPa, annealed | 102 | °C | ASTM D648 |
| 1.8 MPa, annealed | 94.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 107 | °C | ASTM D1525 2 |
| -- | 100 | °C | ASTM D1525 3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm) | 40.0 | % | ASTM D1003 |
| Haze (2000 µm) | > 100 | % | ASTM D1003 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ASTM Classification | PMMA 0231T0V1 | ASTM D788 |
| Note Message | |
|---|---|
| 1 . | Annealing Cycle: 16 hours @ 90°C (194°F) |
| 2 . | 速率 A (50°C/h), 压 力1 (10N) |
| 3 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4085 A TFE 15 | RTP Company | PPA | RTP |
| RTP 800 TFE 5 DEL | RTP Company | Acetal (POM) Homopolymer | RTP |
| UNITIKA Nylon 66 B2040G50 | UNITIKA Plastics Division | Nylon 66 | UNITIKA Nylon 66 |
| Exxtral™ Performance Polyolefin CMU201 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| FRAGOM PR/555 K1 | Crosspolimeri S.p.A. | EVA | FRAGOM |