Bayfill® 500
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Covestro - PUR |
| Trademark: | Bayfill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 67ixkf_Bayfill-500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bayfill 500 is a moldable semi-rigid polyurethane foam system. Bayfill 500 system is designed for backfilling flexible TPU and vinyl skins. Bayfill 500 Component B is reacted with Bayfill 400 Component A to produce instrument panels, center consoles and other protective padding for the automotive industry. As with any product, use of Bayfill 500 system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability for use. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density | 0.200 | g/cm³ |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Hardness - Asker C | 20.0 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Resistance | 800.0 | N/m | JIS K6252 |
| Tensile Strength (3.80 mm) | 0.310 | MPa | JIS K6251 |
| Tensile Elongation (fracture, 3.80mm) | 53 | % | JIS K6251 |
| Thermoset | Nominal Value | ||
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 35 | ||
| Component B | Mixing ratio by weight: 400 |
| Additional Information |
|---|
| Part A Type: Isocyanate (Bayfill 400) Appearance: Dark brown liquid Specific Gravity @ 25°C: 1.24 Viscosity @25°C: 200 mPa-s Part B Type: Polyol (Bayfill 500) Appearance: White liquid Specific Gravity @ 25°C: 1.03 Viscosity @25°C: 1600 mPa-s Hand Mix Reaction Profile at 25°C: Cream Time: 5 sec Gel Time: 38 sec Rise Time: 51 sec Free Rise Density: 64 kg/m³ Molding Parameters: Component Temperature: 40°C polyol/40°C isocyanate Component Pressure: 15 MPa polyol/15 MPa isocyanate Mold Temperature: 40°C Cure Time: 60 sec Degas Range: 35 to 45 sec after start of pour (10 sec) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCW-9205 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| CERTENE™ 9814 Black | Muehlstein | PP, Unspecified | CERTENE™ |
| KRATON® D1117 P | Kraton Polymers LLC | SIS | KRATON® |
| IROGRAN® A 95 E 4861 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| ULTEM™ HU1110 resin | SABIC Innovative Plastics | PEI | ULTEM™ |