| Vyncolit® BXE7665 is a glass fiber filled phenolic molding compound with high mechanical and good thermal properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.90 | g/cm³ | ISO 1183 |
| Apparent Density | 0.63 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.15 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ISO 62 |
| Post Shrinkage | 0.040 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 1.0 | % | ISO 178 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Type | >PF-(GF+MD)65< | ISO 11469 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 22000 | MPa | ISO 527-2 |
| Tensile Stress (Break, Injection Molded) | 101 | MPa | ISO 527-2 |
| Tensile Strain (Break, Injection Molded) | 0.56 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 21000 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 205 | MPa | ISO 178 |
| Compressive Stress | 293 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 3.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (Injection Molded) | 12 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed 1 | > 250 | °C | ISO 75-2/Af |
| 1.8 MPa, Unannealed | 195 | °C | ISO 75-2/Af |
| 8.0 MPa, Unannealed 2 | > 250 | °C | ISO 75-2/Cf |
| 8.0 MPa, Unannealed | 168 | °C | ISO 75-2/Cf |
| CLTE | ASTM E831 | ||
| Flow | 1.4E-5 | cm/cm/°C | |
| Transverse | 3.1E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.48 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.3E+13 | ohms | IEC 60093 |
| Volume Resistivity | 8.1E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 19 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Note Message | |
|---|---|
| 1 . | postcured up to 210°C |
| 2 . | postcured up to 210°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4560 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Niuk YPC4008 | Shanghai Niuk New Plastic Technology Co., Ltd. | Acetal (POM) Copolymer | Niuk |
| Ferro PP LPP20BN51AL | Ferro Corporation | PP, Unspecified | Ferro PP |
| Elastollan® A 1154 DN | BASF Polyurethanes GmbH | TPU-Polyether | Elastollan® |
| Durethan® BKV 330 H2.0 901510 | LANXESS GmbH | Nylon 6 | Durethan® |