Alkathene® XLF197
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Qenos Pty Ltd |
| Trademark: | Alkathene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 67SmDG_Alkathene-XLF197.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
XLF197 is a low density polyethylene designed for the production of thin gauge (less than 20µm) high clarity films. XLF197 does not contain any additives. XLF197 is intended primarily for the manufacture of food wrap films; often an additive is incorporated during the manufacture of film to enhance cling performance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 15 | µm | |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 15 µm, blown film | 180 | MPa | ASTM D882 |
| 2% secant, TD : 15 µm, blown film | 220 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 15 µm, blown film | 12.0 | MPa | ASTM D882 |
| TD : Yield, 15 µm, blown film | 11.0 | MPa | ASTM D882 |
| MD : Broken, 15 µm, blown film | 28.0 | MPa | ASTM D882 |
| TD : Broken, 15 µm, blown film | 13.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 15 µm, blown film | 150 | % | ASTM D882 |
| TD : Broken, 15 µm, blown film | 630 | % | ASTM D882 |
| Dart Drop Impact (15 µm, Blown Film) | 45 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 15 µm, blown film | 190 | g | ASTM D1922 |
| TD : 15 µm, blown film | 82 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45 °, 15.0 µm, blown film) | 76 | ASTM D2457 | |
| Haze (15.0 µm, blown film) | 4.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from blown film processed at a blow up ratio of 2:1. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 D | RTP Company | Nylon 612 | RTP |
| MAXAMID™ EPDM2066UW-BK10 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| Sumitomo Phenolic CF 9040A | Sumitomo Bakelite North America | Phenolic | Sumitomo Phenolic |
| THERMOLAST® V TV9LVN (Series: LTP) | KRAIBURG TPE | SEPS | THERMOLAST® V |
| Sylvin 8200-80UV Red 6257 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |