ExxonMobil™ HDPE HPA 020 Wire & Cable
| Category: | HDPE, UHMW , High Density Polyethylene Resin |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | ExxonMobil™ HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 65vfiK_ExxonMobil-HDPE-HPA-020-Wire-Cable.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HPA 020 is a high density polyethylene grade for medium/high voltage cable sheaths. This grade should be used to mix with linear low density polyethylene to improve environmental stress cracking resistance. Carbon black or ultraviolet stabilizer should be added to make the product conform to the cable sheath specification. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/21.6 kg | 9.0 | g/10 min | ASTM D1238 |
| 190°C/5.0 kg | 0.35 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 27.0 | MPa | ASTM D638 |
| Fracture | 33.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 9.0 | % | ASTM D638 |
| Fracture | 840 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 960 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 129 | °C | ASTM D1525 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 6.5E+16 | ohms·cm | ASTM D257 |
| Dielectric Constant (60 Hz) | 2.10 | ASTM D150 | |
| Dissipation Factor (60 Hz) | 4.0E-4 | ASTM D150 |
| Legal statement |
|---|
| 本产品不宜在与食品接触的应用中使用。本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wanthane® WHT-1685AB | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| Bergamid™ NN-33GF/000 BLACK | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Cheng Yu PP222 | Cheng Yu Plastic Company Limited | PP, Unspecified | Cheng Yu |
| Dynalloy™ 8900-30 | PolyOne Corporation | TPE | Dynalloy™ |
| Osterlene® PPC10-2.1 | Osterman & Company | PP Impact Copolymer | Osterlene® |