Sup-tech AS103
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | Shanghai Suptech Engineering Plastics Co. Ltd. |
| Trademark: | Sup-tech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 64N0gB_Sup-tech-AS103.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sup-tech AS103 is an Acrylonitrile Butadiene Styrene + Nylon (ABS+Nylon) product. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | DIN 53479 |
| Molding Shrinkage | 1.0E-3 to 0.014 | % | DIN 53464 |
| Water Absorption | DIN 53495 | ||
| 23°C, 24 hr | 0.70 | % | |
| Saturation, 23°C | 4.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 70.0 | MPa | DIN 53455 |
| Tensile Strain (Break) | 50 | % | DIN 53452 |
| Flexural Modulus | 2400 | MPa | DIN 53457 |
| Flexural Stress | 90.0 | MPa | DIN 53457 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | kJ/m² | DIN 53453 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | DIN 53461 | ||
| 0.45 MPa, Unannealed | 150 | °C | |
| 1.8 MPa, Unannealed | 55.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Electric Strength | 20 | kV/mm | DIN 53481 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 230 to 265 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® PP HGZ-120SP | Saudi Polymers Company | PP Homopolymer | Marlex® PP |
| MOTIS™ LV | Invibio Inc. | PEEK | MOTIS™ |
| ECOGRAN® PA66 DEMI DULL | Eurocompound Polymers | Nylon 66 | ECOGRAN® |
| KOPA® KN171 | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| LNP™ LUBRICOMP™ KL004 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |