Spartech Polycom SC7-7015U
| Category: | PC , Polycarbonate |
| Manufacturer: | Spartech Polycom |
| Trademark: | Spartech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 646kIO_Spartech-Polycom-SC7-7015U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Spartech SC7-7015U is a low viscosity PC resin for injection molding that features a UV stabilizer. It is heat stabilized and lubricated for good processing characteristics. Polycarbonate resins span a wide range of physical properties that combine to make it one of the toughest, most versatile of all engineering thermoplastics. It is well known for its exceptional impact resistance, plus it has outstanding mechanical, electrical, and optical properties. A very versatile product for a wide variety of applications, Spartech SC7-7015U is recommended for industrial, transportation, sporting goods and electrical/electronic applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 20 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 120 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2340 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 750 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 137 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 271 - 282 | °C | |
| Front Temperature | 282 - 299 | °C | |
| Nozzle Temperature | 277 - 304 | °C | |
| Processing (Melt) Temp | 288 - 316 | °C | |
| Mold Temperature | 71.1 - 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE HP4027J | SABIC Americas, Inc. | LDPE | SABIC® LDPE |
| SEPAZ™ LA40 | Mando Advanced Materials Co., Ltd. | Nylon 66 | SEPAZ™ |
| Novalloy-S S4210 (TypeV) | Daicel Polymer Ltd. | PC+ABS | Novalloy-S |
| Keliren® CM302 | Hangzhou Keli Chemical Co., Ltd. | CPE | Keliren® |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 6213 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |