Bergamid™ A700 G15 HW UF
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergamid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 63Zfgc_Bergamid-A700-G15-HW-UF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bergamid™A700 G15 HW UF is a polyamide 66 (nylon 66) product, which contains a 15% glass fiber reinforced material. It is available in North America, Africa and the Middle East, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.31 | g/cm³ | DIN 53479 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 105 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 261 | °C | ISO 3146 |
| RTI Elec | UL 746 | ||
| 0.400 mm | 65.0 | °C | UL 746 |
| 0.750 mm | 125 | °C | UL 746 |
| 1.50 mm | 125 | °C | UL 746 |
| 3.00 mm | 125 | °C | UL 746 |
| RTI Imp | UL 746 | ||
| 0.400 mm | 65.0 | °C | UL 746 |
| 0.750 mm | 100 | °C | UL 746 |
| 1.50 mm | 110 | °C | UL 746 |
| 3.00 mm | 120 | °C | UL 746 |
| RTI | UL 746 | ||
| 0.400 mm | 65.0 | °C | UL 746 |
| 0.750 mm | 105 | °C | UL 746 |
| 1.50 mm | 115 | °C | UL 746 |
| 3.00 mm | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (CTI) (3.00 mm) | PLC 0 | UL 746 | |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | |||
| 0.400 mm, ALL | V-0 | UL 94 | |
| 0.750 mm, ALL | V-0 | UL 94 | |
| 1.50mm, all | V-0 | Internal method | |
| 3.00 mm, ALL | V-0 | UL 94 | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.60 mm | 960 | °C | IEC 60695-2-13 |
| 3.00 mm 2 | 960 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| These products contain flame retardants which are activated by longer residence times in the cylinder and then can decompose. At interruption of the moulding cycle (approx. >5 min) it is recommended to jet melt completely and to clean the cylinder, e.g. with a standard polyamide. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Holding Pressure | 40.0 - 90.0 | MPa |
| Note Message | |
|---|---|
| 1 . | ±0.03 g/cm³ |
| 2 . | 0.8mm wire |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLARENE G153 | Dongbu Hannong Chemical | PS (GPPS) | SOLARENE |
| Starflam MF0044 | Eurostar Engineering Plastics | PP, Unspecified | Starflam |
| Haysite SMC 42000 | Haysite Reinforced Plastics | Polyester, TS | Haysite SMC |
| HFFR 2002 | Teknor Apex Company | Polyolefin, Unspecified | HFFR |
| Axiall PVC 1551 | Axiall Corporation | PVC, Flexible | Axiall PVC |