Fiberfil® J-60/10/CC/30/E NATL
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 63G512_Fiberfil-J-60-10-CC-30-E-NATL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fiberfil®J-60/10/CC/30/E NATL is a polypropylene homopolymer (PP Homopoly) material, which contains 10% glass fiber reinforcement and 30% calcium carbonate filler. This product is available in North America,. Fiberfil®The main features of J-60/10/CC/30/E NATL are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 4.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 227 | °C | |
| Front Temperature | 182 - 199 | °C | |
| Nozzle Temperature | 182 - 193 | °C | |
| Processing (Melt) Temp | 199 - 232 | °C | |
| Mold Temperature | 32.2 - 71.1 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.00 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw speed: Medium |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECASINT™ 5201 | Ensinger Inc. | PAI | TECASINT™ |
| LNP™ LUBRICOMP™ DFL34 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| LNP™ THERMOCOMP™ MFB82I compound | SABIC Innovative Plastics Europe | PP, Unspecified | LNP™ THERMOCOMP™ |
| POCAN® KU 1-7635 POS 151 000000 | LANXESS GmbH | PC+PBT | POCAN® |
| ESTOPLAST EP 4140GY11 | Ester Industries Ltd. | PBT | ESTOPLAST EP |