Order Products : sales@su-jiao.com
RTP 3400-3
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 62KPGH_RTP-3400-3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unfilled |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13100 | MPa | ASTM D638 |
| Tensile Strength | 128 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength | 148 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 400 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 1200 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 243 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 8.0 | hr | |
| Dew Point | -28.9 | °C | |
| Processing (Melt) Temp | 332 - 366 | °C | |
| Mold Temperature | 65.6 - 121 | °C | |
| Injection Pressure | 82.7 - 124 | MPa |
| Injection instructions |
|---|
| The key to successfully molding this material is to start mold open cycles as soon as the screw reaches its retracted position. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Eastar™ MN021 Natural | Eastman Chemical Company | Copolyester | Eastar™ |
| Latan 23UV | LATI S.p.A. | Acetal (POM) Copolymer | Latan |
| ISOTAL™ C9 | SABIC Innovative Plastics Europe | Acetal (POM) Copolymer | ISOTAL™ |
| LONGLITE® PBT 5630F-104C | CCP Group | PBT | LONGLITE® PBT |
| Hifax CB 237 G 1312 | LyondellBasell Industries | PP Copolymer | Hifax |