Polylink Polymer PBT-11015-GF

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	Polylink Polymers (India) Ltd.
Trademark:	Polylink Polymer
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	61lF8B_Polylink-Polymer-PBT-11015-GF.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Filled PBT compounds are manufacturedbycom pounding PBT with specially treated choppedglass and modified with additives to make parts withhigh mechanical properties, heat resistance and fire resistance.

Excellent flame retardancy.

Good resistance to environmental stress-cracking.

High heat deflection temperature.

Low warpage.

Good mould release.

Good Mechanical Properties.

General Information
Filler / Reinforcement	Filler, 15% filler by weight
Features	Low warpage High ESCR (Stress Cracking Resistance) Good demoulding performance Flame retardancy
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.50 - 1.53	g/cm³	Internal method
Moisture Content	< 800	ppm	Internal method

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break)	73.5 - 78.5	MPa	ASTM D638
Flexural Modulus	5880 - 6370	MPa	ASTM D790
Flexural Strength	118 - 137	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	54 - 56	J/m	ASTM D256

Extrusion	Nominal Value	Unit
Drying Temperature	80.0 - 100	°C
Drying Time	2.0 - 4.0	hr
Cylinder Zone 1 Temp.	215	°C
Cylinder Zone 2 Temp.	220	°C
Cylinder Zone 3 Temp.	230	°C
Cylinder Zone 4 Temp.	240	°C
Cylinder Zone 5 Temp.	245	°C

Extrusion instructions
Zone 6 : 250°C

Resin Grade	Manufacturer	Category	Trademark
SILPURAN® 2112 A/B	Wacker Chemie AG	Silicone	SILPURAN®
VESTAKEEP® Care M40G	Evonik Industries AG	PEEK	VESTAKEEP® Care
ExxonMobil™ PP5722E1	ExxonMobil Chemical	PP Homopolymer	ExxonMobil™
Elastron® V V100.A55.N	Elastron USA, Inc.	TPV	Elastron® V
Hostacom HKC 431N C12334	LyondellBasell Industries	PP Homopolymer	Hostacom