SEPAZ™ C140GP
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | SEPAZ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 617dG4_SEPAZ-C140GP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SEPAZ™ C140GP is a Liquid Crystal Polymer (LCP) product filled with 40% glass fiber. It is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.71 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 135 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.3 | % | ASTM D638 |
| Flexural Modulus | 15600 | MPa | ASTM D790 |
| Flexural Strength | 182 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 271 | °C | ASTM D648 |
| Peak Melting Temperature | 335 | °C | ASTM D2133 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 350 to 360 | °C | |
| Mold Temperature | 30.0 to 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP HI4353L | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| TEKAPPO™ JF1 | Mando Advanced Materials Co., Ltd. | PPE+PS | TEKAPPO™ |
| Sylvin 8764-65 White 184 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Elastron® G G500.A23.B.PA | Elastron USA, Inc. | SEBS | Elastron® G |
| Karina BLUE PVC COMPOUND TR-700D06/972-B-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |