Formolene® L62009A
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation, U.S.A. |
| Trademark: | Formolene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 60Vegf_Formolene-L62009A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Formolene® L62009A is a general-purpose film grade linear low density made using gas-phase technology. The resin exhibits excellent toughness and strength when drawn down to thin gauges. Formolene® L62009A meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.95 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break | 32.8 | MPa | |
| TD : Break | 24.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 520 | % | |
| TD : Break | 780 | % | |
| Dart Drop Impact | 160 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 400 | g | |
| TD | 630 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 33 | ASTM D523 | |
| Haze | 21 | % | ASTM D1003 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Blow-up Ratio | 2.5:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoPrene 80A-4000 | KMI Group Inc. | TPV Alloy | PrimoPrene |
| Unichem 6476 | Colorite Polymers | PVC, Unspecified | Unichem |
| 4PROP® 5C14300 | 4Plas | PP Copolymer | 4PROP® |
| Catalyst CT/1-LR UV | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| EPO-TEK® H77T | Epoxy Technology Inc. | Epoxy | EPO-TEK® |