RTP 6002-65A
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5yZkdP_RTP-6002-65A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. Bondable to PC/ABS, PC, ABS - 65 Shore A |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.00 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 2.3 - 2.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 67 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 8.96 | MPa | ASTM D412 |
| Tensile Elongation 2(Break) | 700 | % | ASTM D412 |
| Tear Strength 3 | 35.0 | kN/m | ASTM D624 |
| Additional Information |
|---|
| Bondable to PC, ABSMoisture Content: <0.02%Peel Strength, ISO 813, 90°, 20 in/min, ABS, Interface Failure: 18.8 pliPeel Strength, ISO 813, 90°, 20 in/min, PC, Overmold Failure: 28.8 pli |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 193 - 227 | °C | |
| Mold Temperature | 21.1 - 48.9 | °C | |
| Injection Pressure | 34.5 - 103 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | C mold, 500 mm/min |
| 2 . | Mouth die C, 500 mm/min |
| 3 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 262 | RTP Company | Nylon 66 | RTP |
| Borealis PP VC105 | Borealis AG | TPO | Borealis PP |
| Braskem PP CP 401 HC | Braskem | PP Impact Copolymer | Braskem PP |
| LNP™ THERMOCOMP™ PFW53U compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |
| ADLAS® O07FFB-00 | A.D. Compound S.p.A. | PP Homopolymer | ADLAS® |