SABIC® LDPE 2402H3W
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5yPcFV_SABIC-LDPE-2402H3W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE 2402H3W is a high gloss, general purpose grade with a high level of anti block and slip agent (E=erucamide). This grade offers good optical properties and a very good draw down ability. Application SABIC® LDPE 2402H3W is typically used for thin high gloss films used for automatic packaging purposes. SABIC® LDPE 2402H3W can typically be used for food applications due to very low migration levels. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.20 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 25 µm, blown film | 190 | MPa | ISO 527-3 |
| TD : 25 µm, blown film | 200 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, blown film | 12.0 | MPa | ISO 527-3 |
| TD : Yield, 25 µm, blown film | 11.0 | MPa | ISO 527-3 |
| MD : Broken, 25 µm, blown film | 28.0 | MPa | ISO 527-3 |
| TD : Broken, 25 µm, blown film | 20.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 25 µm, blown film | > 200 | % | ISO 527-3 |
| TD : Broken, 25 µm, blown film | > 500 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength - Blown FIlm (25.0 µm) | 200 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking - Blown Film (25.0 µm) | g | Internal method | |
| Re-blocking - Blown Film (25.0 µm) | g | Internal method | |
| Tear Strength 1 | ISO 6383-2 | ||
| MD : 25.0 µm | 70.0 | kN/m | ISO 6383-2 |
| TD : 25.0 µm | 35.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 60 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 8.0 | % | ASTM D1003A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film properties have been measured at film of 25 µm with a BUR of 3.The film has been produced on Kiefel IBC blown film line with 200 kg/h. Die size 200 mm, die gap 0.8 mm. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytech & Net VC640 | Polytech & Net Gmbh | EVA | Polytech & Net |
| RTP 2301 C | RTP Company | PUR, Unspecified | RTP |
| MFE® W2-3 | Huachang Polymer Co., Ltd. | Epoxy | MFE® |
| Beetle® PPC120M 9250 | Teknor Apex Company (Chem Polymer) | PP Copolymer | Beetle® |
| Durethan® BKV 50 H EF DUS022 900116 | LANXESS GmbH | Nylon 6 | Durethan® |