Retpol® 6017
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5xLuas_Retpol-6017.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycomp 6017 is an unfilled low flow polypropylene copolymer compound. It has been developed for mouldings requiring long term exposure to water at elevated temperatures and pressures. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.3 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.6 to 1.9 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 82 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 72 | ||
| Shore D, 15 sec, 3.00 mm | 63 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 29.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 300 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 1030 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 55 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.00 mm) | 85.0 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 207H HS | RTP Company | Nylon 66 | RTP |
| RAMTAL PM8103NT7 | Polyram Ram-On Industries | Acetal (POM) Copolymer | RAMTAL |
| Vydyne® R515 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Fainplast PVC PH 80/8-UV | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| DIOSHY® TPU E998M | DIOSHY Co.,Ltd. | TPU-Polyether | DIOSHY® |