XANTAR® LDS 3730
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | XANTAR® LDS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5wlVDD_XANTAR-LDS-3730.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flame Retardant (Halogen free), Black color only, Laser Direct Structuring (LDS)* *The compound is intended specifically for the use in the process of manufacturing conducting path designs according to the German application of the patent 101 32 092 of LPKF Laser & Electronics AG. Please address straight to LPKF Laser & Electronics AG (www.LPKF.de). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 0.60 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.35 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 52.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 30 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C | 40 | kJ/m² | |
| 23°C | 60 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | |||
| -20°C 1 | 25.0 | J | Internal Method |
| 23°C | 35.0 | J | ISO 6603-2 |
| 23°C 2 | 25.0 | J | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 122 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Relative Permittivity (1.00 GHz) | 3.00 | IEC 60250 | |
| Dissipation Factor (1.00 GHz) | 5.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VB | ||
| 0.500 mm | HB |
| Note Message | |
|---|---|
| 1 . | Part with rib, Based on ISO 6603-2 |
| 2 . | Part with rib, Based on ISO 6603-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS 77 K4 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Wellamid® MRGF1647-BK1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| UBESTA 3020X29L | UBE Industries, Ltd. | Nylon 12 | UBESTA |
| Clariant Acetal HP-MF9 | Clariant Corporation | Acetal (POM) Homopolymer | Clariant Acetal |
| SCHULADUR® HT GF 30 FR 5 black | A. Schulman Europe | PCT | SCHULADUR® |