Ultramid® A3SK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5uhNKV_Ultramid-A3SK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Very easy flowing injection moulding grade for rapid production of thin-walled technical parts (eg housings and small components) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 135 | -- | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 8.0 to 9.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.5 to 3.1 | -- | % | |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 150 | -- | cm³/g | ISO 307 |
| Mold Shrinkage - constrained 1 | 0.65 | -- | % |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Maximum Service Temperature - short cycle operation | 200 | -- | °C | |
| Temperature Index - at 50% loss of tensile strength | IEC 60216 | |||
| -- 2 | 99 | -- | °C | |
| -- 3 | 118 | -- | °C |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3500 | 1600 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 95.0 | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 4.3 | 20 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | 15 | > 50 | % | ISO 527-2/50 |
| Flexural Modulus | 3200 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 4.0 | -- | kJ/m² | |
| 23°C | 4.0 | 30 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 80°C) | 7.0E-5 to 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1700 | -- | J/kg/°C | |
| Thermal Conductivity | 0.33 | -- | W/m/K | DIN 52612 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.20 | 5.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.025 | 0.20 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test box with central gating, dimensions of base (107*47*1,5) mm, processing conditions: TM = 290°C, TW = 60°C |
| 2 . | 20000 h |
| 3 . | 5000 h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SuperLite® SL551800-100 (10.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| Nypol® PA A3 BRC0003 NR344 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| AIE PA66 60G3F | Asia International Enterprise (Hong Kong) Limited | Nylon 66 | AIE PA66 |
| Badaflex® TPE-S 30A 1000LD | Bada AG | TPE | Badaflex® |
| LARIPUR® LPR 7560 | COIM S.p.A. | TPU-Polyether | LARIPUR® |