LITAC-A® 100PCF
| Category: | AS , Acrylonitrile Styrene Copolymer |
| Manufacturer: | Nippon A&L Inc. |
| Trademark: | LITAC-A® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5tuuPz_LITAC-A-100PCF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LITAC-A®100PCF is an acrylonitrile styrene copolymer (AS) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. LITAC-A®The main characteristics of 100PCF are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.07 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.20 - 0.50 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 127 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 71.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 3600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 124 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.5 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 85.0 | °C | ISO 75-2/A |
| CLTE - Flow (23 to 80°C) | 6.0E-5 | cm/cm/°C | JIS K7197 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Ball Pressure Registration Temperature: 95°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | > 3.0 | hr | |
| Rear Temperature | 210 - 250 | °C | |
| Middle Temperature | 210 - 250 | °C | |
| Front Temperature | 210 - 250 | °C | |
| Mold Temperature | 50.0 - 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax 6331NW | LyondellBasell Industries | PP Homopolymer | Pro-fax |
| VAMPCARB 3028 V0 | Vamp Tech | PC | VAMPCARB |
| Celstran® PP-GF40-0403 P10/10 | Celanese Corporation | PP, Unspecified | Celstran® |
| Karina BLUE PVC COMPOUND 804-06/115-CRM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupolen UHM 5000 | LyondellBasell Industries | UHMWPE | Lupolen |