CYCOLOY™ MC8800 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5sc32g_CYCOLOYMC8800resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PC/ABS, high heat, high impact, low CTE. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (265°C/5.0 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.40 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 55.0 | MPa | ISO 527-2/5 |
| Fracture | 58.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 4.2 | % | ISO 527-2/5 |
| Fracture | 100 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 3100 | MPa | ISO 178 |
| Flexural Stress | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 35 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact 3 | ISO 180/1A | ||
| -30°C | 10 | kJ/m² | ISO 180/1A |
| 23°C | 30 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 118 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 135 | °C | ISO 306/B50 |
| -- | 137 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 30 - 80 | % | |
| Rear Temperature | 260 - 271 | °C | |
| Middle Temperature | 266 - 288 | °C | |
| Front Temperature | 271 - 299 | °C | |
| Nozzle Temperature | 271 - 299 | °C | |
| Processing (Melt) Temp | 282 - 299 | °C | |
| Mold Temperature | 77 - 99 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.038 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 sp=62mm |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecopet® PT70 GR15 NL100 PR | Eurotec Engineering Plastics | PET | Tecopet® |
| Next Nylon 6 Prime Series NGF2 20-01GY | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Axiall PVC 12882 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Axiall PVC 18841 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Braskem PP DC707.01 | Braskem Europe GmbH | PP Impact Copolymer | Braskem PP |