Edgetek™ MP-20GF/000 BLK
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5sa3sw_EdgetekMP20GF000BLK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% glass fiber reinforced MPPO compound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 100 | MPa | ASTM D638 |
| Flexural Modulus 2 | 6200 | MPa | ASTM D790 |
| Flexural Strength 3 | 160 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 150 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | HB | UL 94 | |
| 3.0 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 270 - 300 | °C | |
| Middle Temperature | 270 - 300 | °C | |
| Front Temperature | 270 - 300 | °C | |
| Mold Temperature | 65 - 95 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN 3O 51 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Topolymer® M-601J | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| Wellamid® GF33-66/6 XE-BKDX9 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| COPYLENE® CH350LN-01 | Phillips 66 | PP Homopolymer | COPYLENE® |
| LNP™ THERMOCOMP™ WC006 compound | SABIC Innovative Plastics | Polyester, TP | LNP™ THERMOCOMP™ |