BCC Resins BC 6005
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | BCC Products Inc. |
| Trademark: | BCC Resins |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5s6gti_BCC-Resins-BC-6005.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BC 6005 is a snow white thixotropic epoxy resin designed specifically for quality reproduction of a variety of surfaces. A room temperature cure system that offers ample working time yet affords quick-tack for lamination. BC 6005 may be applied easily with a brush or troweled to a thickness of 1/8" or less on vertical surfaces or over sharp radii without sag or fear of run-off. When cured, this resin system provides a hard tough chip-resistant surface. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.50 | g/cm³ | ASTM D792 |
| -- | 1.49 | g/cm³ | ASTM D1505 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 89 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Ultimate) | 46.9 | MPa | ASTM D638 |
| Flexural Modulus | 6620 | MPa | ASTM D790 |
| Flexural Strength (Break) | 61.4 | MPa | ASTM D790 |
| Compressive Strength | 90.3 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 58.9 | °C | ASTM D648 |
| CLTE - Flow | 7.7E-5 | cm/cm/°C | ASTM D696 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 1.0, Mix Ratio by Volume: 1.0 | ||
| Resin | Mix Ratio by Weight: 6.0, Mix Ratio by Volume: 4.0 | ||
| Pot Life (25°C) | 18 to 22 | min | |
| Demold Time (25°C) | 480 to 720 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POYAD AS101 | Pooya Polymer Tehran | PP Homopolymer | POYAD |
| RTP 1007 TFE 10 | RTP Company | PBT | RTP |
| SUNFROST® KD55JB | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNFROST® |
| FLEXITEQ™ F67A011UV | Marplex Australia Pty. Ltd. | TPV | FLEXITEQ™ |
| Lastilac AR-V0E | LATI S.p.A. | ABS | Lastilac |