SABIC® HDPE B5823
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5raZoM_SABICHDPEB5823.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE B5823 is developed for blow moulding consumer packaging up to 5 l, combining high stiffness and a good ESCR level. This grade is suitable for packaging the majority of detergents, cleaners, shampoos and cosmetics. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.958 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.16 | g/10 min | ISO 1133 |
| 190°C/21.6 kg | 23 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.89 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance 1(75°C, 1.00 mm, Rhodacal-DS10) | 13.0 | hr | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1150 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00mm, molded | 28.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 2.00mm, molded | 22.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 1000 | % | ISO 527-2/1BA/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 6.0 | kJ/m² | ISO 180/1A |
| 23°C | 12 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 85.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 48.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 128 | °C | ISO 306/A50 |
| -- | 79.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 133 | °C | DIN 53765 |
| Enthalpy Change | 215 | J/g | DIN 53765 |
| Note Message | |
|---|---|
| 1 . | 3 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 66 GF 30 HI | Plastcom | Nylon 66 | SLOVAMID® 66 |
| Ultramid® A3WG7 HP R01 BK20560 | BASF Corporation | Nylon 66 | Ultramid® |
| DOW™ Electrical & Telecommunications DHDA-7707 BK | The Dow Chemical Company | Polyolefin, Unspecified | DOW™ Electrical & Telecommunications |
| Durethan® C 1206 00000 | LANXESS GmbH | PC+PET | Durethan® |
| Kepamid® 2300SU | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |