Lion Idemitsu Composites PPS T541M1
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Lion Idemitsu Composites Co., Ltd. |
| Trademark: | Lion Idemitsu Composites PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5qp3ZB_Lion-Idemitsu-Composites-PPS-T541M1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lion Idemitsu Composites PPS T541M1 is a Polyphenylene Sulfide (PPS) product filled with 60% carbon\mineral. It is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.60 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow | 0.40 | % | |
| Flow | 0.15 | % | |
| Water Absorption (23°C, 24 hr) | > 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 102 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 160 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.60 | % | ISO 527-2 |
| Flexural Modulus | 35800 | MPa | ISO 178 |
| Flexural Stress | 295 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 4.3 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 269 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 4.0E-6 | cm/cm/°C | |
| Transverse | 2.4E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | < 1.0E+2 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.830 mm) | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flowability 2(1.00 mm) | 8.00 | cm | Internal Method |
| Note Message | |
|---|---|
| 1 . | Internal Method |
| 2 . | Thickness 1mm, Cylinder temperature 320°C, Injection pressure 100MPa, Mold temperature 135°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1765B | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| DynaPath™ C2010CF | Polymer Dynamix | PC | DynaPath™ |
| LNP™ LUBRICOMP™ FX86496 compound | SABIC Innovative Plastics | PE, Unspecified | LNP™ LUBRICOMP™ |
| Rotuba CAB B9024 (13% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |
| Elastocon® 2855 | Elastocon TPE Technologies | TPE | Elastocon® |