Lasulf LASULF G/15
| Category: | PSU , Polysulfone |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Lasulf |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5mQ4Gu_Lasulf-LASULF-G-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polysulphone (PSU). UL94 V-0 classified, halogens free. Glass fibres. Low smoke toxicity index and optical density. Very high dimensional stability. Low thermal expansion coefficient. Very high thermal resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.65 to 0.85 | % | |
| Flow : 2.00 mm | 0.20 to 0.45 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 5500 | MPa | |
| 60°C | 5300 | MPa | |
| 90°C | 5200 | MPa | |
| 120°C | 5100 | MPa | |
| 150°C | 4700 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 90.0 | MPa | |
| Break, 60°C | 80.0 | MPa | |
| Break, 90°C | 75.0 | MPa | |
| Break, 120°C | 65.0 | MPa | |
| Break, 150°C | 50.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 2.3 | % | |
| Break, 60°C | 2.0 | % | |
| Break, 90°C | 2.0 | % | |
| Break, 120°C | 1.9 | % | |
| Break, 150°C | 1.8 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 3.5 | kJ/m² | |
| 23°C | 3.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 40 | kJ/m² | |
| 23°C | 30 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 65 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 185 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 175 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 160 | °C | |
| Vicat Softening Temperature | 185 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 1.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Oxygen Index | 35 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 300 to 330 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borealis PP HE465FB | Borealis AG | PP Homopolymer | Borealis PP |
| Karina GREEN COLOR CONCENTRATE -E 40/272-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ EL003 compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |
| Plastiglas Stonia® | Plastiglas de Mexico S.A de C.V. | Acrylic, Unspecified | Plastiglas |
| POLYFLON™ F-201 | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |