Stirolan DF AE V0 1.6
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Stirolan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5mHSML_Stirolan-DF-AE-V0-1-6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polystyrene impact modified, flame retardant UL 94 V0 at 1.6 mm rating. Polybrominphenyle-free and polybromindiphenylether-free. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 20.0 | MPa | |
| Break | 22.0 | MPa | |
| Tensile Elongation 2(Break) | 40 | % | ASTM D638 |
| Flexural Modulus 3 | 2000 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 34.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.20 mm | 30 | J/m | |
| 23°C, 3.20 mm | 50 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 88.0 | °C | ASTM D1525 5 |
| CLTE - Flow (23 to 55°C) | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Relative Permittivity (1 MHz) | 2.30 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1038 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| tefabloc® TP SD 333 65A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| ULTEM™ 1010M resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Nypol® PA B3 HL NTLA010 NT308 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Hanwha Total PE EP32 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LLDPE | Hanwha Total PE |