Nypol® PA A3 ST HS PRTA011 NR365 MSP
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5lgiiQ_Nypol-PA-A3-ST-HS-PRTA011-NR365-MSP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lubricated polyamide 6.6 in black color, thermo stabilized, high impact strength (ST), excellent mechanical properties, high tenacity and elongation, good set of thermal properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.09 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow : 3.20 mm | 1.4 | -- | % | |
| Across Flow : 3.20 mm | 1.2 | -- | % | |
| Water Absorption (Equilibrium) | 1.2 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | 70 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ASTM D638 | |||
| -40°C | 2120 | 2630 | MPa | |
| 23°C | 1900 | 1100 | MPa | |
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 75.0 | 78.0 | MPa | |
| Yield, 23°C | 50.0 | 40.0 | MPa | |
| -- | 50.0 | 38.0 | MPa | |
| Tensile Elongation | ASTM D638 | |||
| Yield, -40°C | 10 | 14 | % | |
| Yield, 23°C | 5.0 | 40 | % | |
| Break, -40°C | 20 | 31 | % | |
| Break, 23°C | 32 | > 50 | % | |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 2150 | 2850 | MPa | |
| 23°C | 1900 | 830 | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (Area) | ASTM D256 | |||
| -40°C | 18.0 | -- | kJ/m² | |
| 23°C | 71.5 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 230 | -- | °C | |
| 1.8 MPa, Unannealed | 61.0 | -- | °C | |
| Melting Temperature | 250 to 265 | -- | °C | ASTM D2117 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | |||
| -- | 5.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 270 to 285 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1275 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Tecnoflon® T 538 | Solvay Specialty Polymers | Fluorelastomer | Tecnoflon® |
| Vi-Chem PVC VIR 6186 | Vi-Chem Corporation | PVC, Rigid | Vi-Chem PVC |
| VENELENE® 7000F | Poliolefinas Internacionales, C.A. (Polinter) | HDPE | VENELENE® |
| Durethan® AKV 35 H2.0 SR1 901510 | LANXESS Corporation | Nylon 66 | Durethan® |