Ultramid® 8232G HS FR BK-102
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5kUgRW_Ultramid-8232G-HS-FR-BK-102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8232G HS FR BK-102 is a 25% glass fiber reinforced, heat stabilized, flame retardant pigmented black PA6 injection molding compound exhibiting excellent melt stability characteristics. It combines flame retardant ability with an excellent balance of high strength, stiffness and heat distortion temperature. Applications Ultramid 8232G HS FR BK-102 is generally recommended for applications such as connectors, terminal blocks, switches and receptacles, coil bobbins, and appliance housings. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.62 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | |
| Water Absorption | ASTM D570 | ||
| Saturation | 4.0 | % | |
| Equilibrium, 50% RH | 1.1 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 145 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.5 | % | ASTM D638 |
| Flexural Modulus (23°C) | 9170 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 210 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 205 | °C | ASTM D648 |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| RTI Elec | UL 746 | ||
| 0.840 mm | 130 | °C | |
| 1.50 mm | 130 | °C | |
| 2.50 mm | 130 | °C | |
| 3.00 mm | 130 | °C | |
| RTI Imp | UL 746 | ||
| 0.840 mm | 115 | °C | |
| 1.50 mm | 115 | °C | |
| 2.50 mm | 115 | °C | |
| 3.00 mm | 115 | °C | |
| RTI Str | UL 746 | ||
| 0.840 mm | 105 | °C | |
| 1.50 mm | 115 | °C | |
| 2.50 mm | 115 | °C | |
| 3.00 mm | 120 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.840 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 2.50 mm | V-0 5VA | ||
| 3.00 mm | V-0 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC/ABS-FR1 | Polymer Resources Ltd. | PC+ABS | PRL |
| Ravathane R210A80UV | RAVAGO Kimya Plastik Sanayi ve Ticaret A.S. | TPU-Polyether | Ravathane |
| RTP 103CC UV | RTP Company | PP, Unspecified | RTP |
| Zytel® FN718 BK230A | DuPont Performance Polymers | Nylon 66 | Zytel® |
| ULTEM™ 1000F resin | SABIC Innovative Plastics | PEI | ULTEM™ |