AVP™ RY633CP
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | AVP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5hpkX2_AVP-RY633CP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AVP™ RY633CP is a Polyamide 6 (Nylon 6) product filled with 33% glass fiber. It can be processed by injection molding and is available in North America. Primary characteristic: heat stabilizer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Ultimate, 3.18 mm) | 138 | MPa | ASTM D638 |
| Flexural Modulus 2(3.18 mm, 50.8 mm Span) | 6210 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 69 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 210 | °C | ASTM D648 |
| Melting Temperature | 216 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 227 to 260 | °C | |
| Middle Temperature | 243 to 277 | °C | |
| Front Temperature | 260 to 293 | °C | |
| Nozzle Temperature | 260 to 293 | °C | |
| Processing (Melt) Temp | 260 to 293 | °C | |
| Mold Temperature | 65.6 to 110 | °C | |
| Back Pressure | 0.172 to 1.03 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9610-80 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NuSil CF3-3521 | NuSil Technology | Silicone | NuSil |
| 3M™ Dyneon™ Fluoroplastic THV 815GZ | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroplastic |
| EVAL™ SP292 | Kuraray Co., Ltd. | EVOH | EVAL™ |
| LNP™ LUBRICOMP™ DFL42 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |