SilTRUST® TSE3664K
| Category: | Silicone , Silicone |
| Manufacturer: | Momentive Performance Materials Inc. |
| Trademark: | SilTRUST® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5hkQ6R_SilTRUST-TSE3664K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SilTRUST TSE3664K is a two-component condensation cure silicone rubber designed for electric potting. TSE3664 K cures at room temperature to form an elastic flame retardant rubber and adheres various types of materials such as metal, plastics, glass and ceramics without the use of primers. Key Features and Benefits
Potential Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density | 1.41 | g/cm³ |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 60 |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength | 3.00 | MPa | |
| Tensile Elongation (Break) | 70 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Conductivity | 0.40 | W/m/K | Internal Method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+17 | ohms·cm | |
| Electric Strength | 26 | kV/mm | |
| Dielectric Constant (60 Hz) | 3.10 | ||
| Dissipation Factor (60 Hz) | 0.010 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Volume: 10 Mix Ratio by Weight: 7.5 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 1 | Blue | ||
| -- 2 | Grey | ||
| Density | |||
| -- 3 | 1.08 | g/cm³ | |
| -- 4 | 1.41 | g/cm³ | |
| Viscosity | |||
| -- 5 | 0.010 | Pa·s | |
| -- 6 | 3.0 | Pa·s | |
| -- 7 | 4.0 | Pa·s | |
| Curing Time (23°C) | 72 | hr | |
| Tack Free Time | 20 | min | |
| Pot Life | 6.0 | min |
| Note Message | |
|---|---|
| 1 . | Part B |
| 2 . | Part A |
| 3 . | Part B |
| 4 . | Part A |
| 5 . | Part B |
| 6 . | Mixed |
| 7 . | Part A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDB 501 | Marco Polo International, Inc. | HDPE | MARPOL® |
| Maxelast® P1755P | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TOTAL Polyethylene LDPE 1070 MN 18 C | TOTAL Refining & Chemicals | LDPE | TOTAL Polyethylene |
| VAMPAMID HT3 3028 V0 | Vamp Tech | Nylon, Unspecified | VAMPAMID |
| ASI POLYETHYLENE CP 879-01 | A. Schulman Inc. | LDPE | ASI POLYETHYLENE |