Propafilm™ MVG80
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5hSDxA_Propafilm-MVG80.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Metallizable Film Biaxially oriented polypropylene (BOPP) film co-extruded on both sides with heat sealable polyolefinic polymers. MVG is suitable for vacuum metallizing with aluminium and other substances. The metallized surface may be over-printed or lacquered. MVG80 is normally metallized for use in laminations with other substrates, particularly Propafilm RGP. MVG120 can be metallized for use as a single web film in horizontal form-fill-and-seal applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | Internal method | ||
| Flow : 129°C, 1 minute | 6.0 | % | Internal method |
| Transverse flow : 129°C, 1 minute | -1.0 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| With itself-dynamic, outer layer/outer layer | 0.50 | ASTM D1894 | |
| With itself-static, outer layer/outer layer | 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD | 2690 | MPa | ASTM D882 |
| 1% secant, TD | 2290 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield | 239 | MPa | ASTM D882 |
| TD : Yield | 190 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Fracture | 90 | % | ASTM D882 |
| TD : Fracture | 130 | % | ASTM D882 |
| Seal Strength 4 | 0.14 | N/mm | Internal method |
| Seal Initiation Temperature 5 | 116 - 146 | °C | Internal method |
| Oxygen Permeability (23°C, 0% RH) | 58 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate (38°C, 90% RH) | 7.4 | g/m²/24 hr | ASTM F1770 |
| Corona Treatment | 38 | dyne/cm | Internal method |
| Film thickness | 80.0 | Internal method | |
| Yield | 55.0 | m²/kg | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°) | 105 | ASTM D2457 | |
| Haze 6 | 2.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 10%/min |
| 2 . | 50%/min |
| 3 . | 50%/min |
| 4 . | 265°F; 2secs; 15lb/in²; untreated to untreated |
| 5 . | 2secs; 15lb/in²; untreated to untreated |
| 6 . | Wide angle, 2.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong Aobang TPU-Polyester 65-A | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Polyester | Shandong Aobang TPU-Polyester |
| TEREZ PA 6 7400 GK 50 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Colorite 11 Series 8011 | Colorite Polymers | PVC, Unspecified | Colorite 11 Series |
| Desmopan® DP 3868D | Covestro - PUR | TPU-Polyester | Desmopan® |
| ELASTOSIL® RT 426 | Wacker Chemie AG | Silicone | ELASTOSIL® RT |