KRALASTIC® TE-2200
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Nippon A&L Inc. |
| Trademark: | KRALASTIC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5gpGml_KRALASTIC-TE-2200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KRALASTIC® TE-2200 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific or North America for injection molding. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.10 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 28.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.50 to 0.70 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 105 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 39.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 1700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 58.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 73.0 | °C | ISO 75-2/A |
| CLTE - Flow (23 to 80°C) | 8.2E-5 | cm/cm/°C | JIS K7197 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm) | 89.0 | % | ISO 13468-1 |
| Haze (2000 µm) | 4.5 | % | ISO 14782 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 80.0 | °C | |
| Drying Time | > 3.0 | hr | |
| Rear Temperature | 180 to 220 | °C | |
| Middle Temperature | 180 to 220 | °C | |
| Front Temperature | 180 to 220 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NOVADURAN® 5010GN1-30AM2 | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| KOPA® KN333G15 | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| LNP™ LUBRILOY™ U2000A compound | SABIC Innovative Plastics | PPA | LNP™ LUBRILOY™ |
| POLYFLON™ F-301 | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |
| GELOY™ XP4034 resin | SABIC Innovative Plastics | ASA+PC | GELOY™ |