Ultradur® B 4406 G6
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultradur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5gaoGv_Ultradur-B-4406-G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Injection molding grade with 30 % glass fibers for parts requiring enhanced fire resistance (eg potentiometer parts, plug-and-socket connectors, switches). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.40 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Viscosity Number 1 | 108 | cm³/g | ISO 307 |
| Mold Shrinkage 2 | |||
| free, longitudinal | 0.20 | % | |
| free, transverse | 1.0 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Temperature index- at 50% loss of tensile strength | IEC 60216 | ||
| -- 3 | 125 | °C | IEC 60216 |
| -- 4 | 150 | °C | IEC 60216 |
| Maximum operating temperature- short cycle operation | 210 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability by Electrical Sources of Ignition (4.00 mm) 5 | BH2 | IEC 60707 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Automotive Materials (> 1.00 mm) | Pass | FMVSS 302 | |
| ISO Type | PBT, MFGHLNR, 11-110, GF30 | ISO 7792 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Screw Speed | mm/sec |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 220 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 145 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.3 | % | ISO 527-2 |
| Tensile Creep Modulus 6(1000 hr) | 7500 | MPa | ISO 899-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 55 | kJ/m² | ISO 179/1eU |
| 23°C | 60 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 205 | °C | ISO 75-2/A |
| Melting Temperature | 223 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 80°C) | 2.0E-5 - 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1400 | J/kg/°C | |
| Thermal Conductivity | 0.32 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.90 | IEC 60250 | |
| 1 MHz | 3.90 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 2.0E-3 | IEC 60250 | |
| 1 MHz | 0.015 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | ||
| Solution a | 200 | V | IEC 60112 |
| Solution B | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.400 mm | V-0 | IEC 60695-11-10, -20 | |
| 1.60 mm | V-0 | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 120 | °C | |
| Drying Time | 4.0 | hr | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 240 | °C | |
| Middle Temperature | 245 | °C | |
| Front Temperature | 250 | °C | |
| Nozzle Temperature | 250 | °C | |
| Processing (Melt) Temp | 250 - 275 | °C | |
| Mold Temperature | 60.0 - 100 | °C |
| Injection instructions |
|---|
| Residence time: <10 min. |
| Note Message | |
|---|---|
| 1 . | solution 0,005 g/ml Phenole/1,2 Dichlorbenzol 1:1 |
| 2 . | plate with film gate 150*150*3 mm³ |
| 3 . | 20000 h |
| 4 . | 5000 h |
| 5 . | Method BH |
| 6 . | strain <= 0,5%, 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 204 HS | RTP Company | Nylon 66 | RTP |
| Next ABS SX-02BK | Next Polymers Ltd. | ABS | Next ABS |
| Grilon® B 70 GFE 30 H | EMS-GRIVORY | Nylon 6 | Grilon® |
| KumhoSunny PBT/ABS HBG5723FR | Shanghai KumhoSunny Plastics Co., Ltd. | ABS+PBT | KumhoSunny PBT/ABS |
| Lion Idemitsu Composites PPS C-230SE | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |